High Stress Relaxation Resistance Copper Alloy CAC™ 5

Features

  • The copper alloy specifically desgned for terminals with a wire barrel
  • Excellent stress relaxation resistance, suitable for automotive applications. Compliant to JASO-C400 class.
  • High strength equivalent to phosphorous bronze (C5210) and brass (C2600)
  • Registered with the CDA (Copper Development Association)
  • A variety of pre-tin plating products are available. Has the plating types of New Tin Reflow and normal tin reflow

Applications

  • Special terminals for consumer and industrial use

Nominal Compositions

Cu-0.8Ni-1.2Sn-0.07P (mass%)

Characteristics

Physical Properties

Specific Gravity 8.9
Coefficient of Thermal Expansion (293~573K) 17.7 x 10 -6 K Thermal
Conductivity (293K) 166 W/m.K
Electrical Resistivity (293K) 43.1 nΩ.m
Electrical Conductivity (293K) 40 %IACS
Modulus Elasticity (293K) 130 GPa
  • *Note: The above are typical characteristics.

Mechanical Properties

Temper Tensile Strength
MPa
Yield Strength
MPa
Elongation
%
Vickers Hardness
MHv: 4.9N
H/SP 500–590 530 7 min 155–185
EH/SP 540–630 570 5 min 165–200
  • *Note 1: Figures in yield strength are nominal values.
  • *Note 2: The above tensile strength and hardness are standard specifications. Technical specifications will be determined according to consumer requests.

90°V-Type Bend-Formability (MBR)

Temper Good Way Bad Way
H/SP 0 0
EH/SP 0.2 0.2
  • *Note: The above are typical characteristics. The value slightly varies depending on the thickness of specimens.